Brass Copper Fittings (INDIA) Home Email Sitemap
Home About Us Products Resources Email Contact Us Sitemap
Copper Turned Parts | Copper Fittings | Copper Pressed Parts | Copper Casting | Bronze Fittings | Copper Washers | Copper Bronze Grounding Parts | Bronze Casting | Copper Electrical Components | Brass Electrical Components | Brass Turned Parts | Brass Fasteners | Brass Casting | Copper Casting Alloys | Brass Wires Rods Alloys | Brass Hardware Fittings | Brass Sanitary Pipe Fittings | Brass Hose Fittings | Stainless Steel Fittings | Brass Moulding Inserts | Copper Lugs Terminals
Copper Turned Parts
Copper Fittings
Copper Pressed Parts
Copper Casting
Bronze Fittings
Copper Washers
Copper Bronze Grounding Parts
Bronze Casting
Copper Electrical Components
Brass Electrical Components
Brass Turned Parts
Brass Fasteners
Brass Casting
Copper Casting Alloys
Brass Wires Rods Alloys
Brass Hardware Fittings
Brass Sanitary Pipe fittings
Brass Hose Fittings
Stainless Steel Fittings
Brass Moulding Inserts
Copper Lugs Terminals
              Aluminum Bronze C95400 (9C)

Aluminum Bronze C95400 (9C)   Copper Alloy No. C95400   Aluminum Bronze C95400 (9C)

Aluminum Bronze 9C , CDA 954 , CuAl10Fe

ASTM B 505 , ASTM B 271
Chemical Composition % by weight
Element Nominal Minimum Maximum
Aluminum 11 10 11.5
Copper 85 83 .35
Iron 83 81 85
Manganese - - .20
Nickel 7 6 8
Application for Castings
Bearings, gears, worm gears, bushings, wear plate, valve seats and guides, pickling hooks.
Mechanical Properties (as cast)
M07 - As Continuous Cast
Hardness* Brinell Hardness (3000 kg load) 170
Tensile Strength** KSI 85 min
Yield Strength** KSI (0.5% Ext. under load) 32 min
Elongation** % in 2 inch 10 min
**Test values are nominal approximations and depend on specimen size and orientation.
Physical Properties
Thermal Conductivity BTU/ (sq ft-ft-hr-F) 33.9
Specific Heat BTU/lb/ºF @ 68F .10
Thermal Expansion Per °F from 68 F to 572 F .000009
Density lb/cu in @ 68 F .269
Electrical Conductivity* (Annealed) % IACS @ 68 F 13
Modulus of Elasticity KSI 15,500
*Volume basis
Fabrication Practices
Stress relieving temperature 600 F or 316 C
Time at temperature 1 hour per inch of section thickness
Responds to heat treatment Yes
Solution heat treating temperature 1600-1675 F or 870-910 C
Time at temperature 1 hour per inch of section thickness
Quenching medium Water
Annealing temperature 1150-1225 F or 620-660 C
Time at temperature 1 hour per inch of section thickness
Machinability rating (Free Cutting Brass=100) 60
Suitability for being joined by: Soldering/Good
Brazing/Good
Oxyacetylene Welding/Not Recommended
Carbon Arc Welding/Fair
Gas Shielded Arc Welding/Very Good
Coated Metal Arc Welding/Good
The values listed above represent reasonable approximations suitable for general engineering use. Due to commercial variations in composition and to manufacturing limitations, they should not be used for specification purposes. See applicable A.S.T.M. specification references.

C95400 Aluminum Bronze, 932 Bronze, Bronze Alloys, C360 Brass, C10100 Copper, Copper C11000, C14500, C95500, Astm B584, C83600, C95800, C36000, C93200 Bronze, C93200, Leaded Bronze, Bronze Rod, Phosphor Bronze, Phosphorous Bronze, Naval Brass, Uns C95400 Related words : C95400 Aluminum Bronze, 932 Bronze, Bronze Alloys, C360 Brass, C10100 Copper, Copper C11000, C14500, C95500, Astm B584, C83600, C95800, C36000, C93200 Bronze, C93200, Leaded Bronze, Bronze Rod, Phosphor Bronze, Phosphorous Bronze, Naval Brass, Uns C95400
Please contact us for all your needs of

Aluminum Bronze C95400 (9C)

at best prices from India. We are the biggest foundry casting alloy indian manufacturers exporters foundries in Jamnagar of

Aluminum Bronze C95400 (9C)


Bearing Bronze C93200·SAE 660 Bearing Bronze C93200·SAE 660 Manganese Bronze·C86300 Manganese Bronze·C86300
 Designed & maintained by:  www.conextechno.com 
Home | About Us | Products | Resources | Email | Contact Us | Sitemap
                   +