Brass Copper Fittings (INDIA) Home Email Sitemap
Home About Us Products Resources Email Contact Us Sitemap
Copper Turned Parts | Copper Fittings | Copper Pressed Parts | Copper Casting | Bronze Fittings | Copper Washers | Copper Bronze Grounding Parts | Bronze Casting | Copper Electrical Components | Brass Electrical Components | Brass Turned Parts | Brass Fasteners | Brass Casting | Copper Casting Alloys | Brass Wires Rods Alloys | Brass Hardware Fittings | Brass Sanitary Pipe Fittings | Brass Hose Fittings | Stainless Steel Fittings | Brass Moulding Inserts | Copper Lugs Terminals
Copper Turned Parts
Copper Fittings
Copper Pressed Parts
Copper Casting
Bronze Fittings
Copper Washers
Copper Bronze Grounding Parts
Bronze Casting
Copper Electrical Components
Brass Electrical Components
Brass Turned Parts
Brass Fasteners
Brass Casting
Copper Casting Alloys
Brass Wires Rods Alloys
Brass Hardware Fittings
Brass Sanitary Pipe fittings
Brass Hose Fittings
Stainless Steel Fittings
Brass Moulding Inserts
Copper Lugs Terminals
              C14500 Tellurium Copper

C14500 Tellurium Copper   Copper No. C14500   C14500 Tellurium Copper

Tellurium Copper , CDA 145 ASTM B 301

Nominal Chemical Composition % by weight
Copper (incl. Silver) Phosphorus Tellurium
99.7 .008 .55
Applications
Forgings, screw machine products and parts requiring high conductivity, extensive machining, corrosion resistance, copper color, or a combination of these; electrical connectors, motor and switch parts, plumbing fittings, soldering coppers, welding torch tips, transistor bases and furnace brazed articles.
Mechanical Properties
Typical for 1" solid diameter Hard (35%) Temper
Hardness* Rockwell F Scales 48
Tensile Strength** KSI 48
Yield Strength ** KSI 44
Elongation** % in 2 inch 20
*Hardness conversions are approximate

**Test values are nominal approximations and depend on specimen size and orientation.
Physical Properties
Thermal Conductivity BTU/ (sq ft-ft-hr-F) 20.5
Specific Heat BTU/lb/ºF @ 68F .092
Thermal Expansion Per °F from 68 F to 212 F .0000095
Density lb/cu in @ 68 F .323
Electrical Conductivity % IACS @ 68 F 93
Modulus of Elasticity KSI 17,000
*Volume basis
Fabrication Practices
Capacity for being cold worked Good
Capacity for being hot formed Good
Hot forgeability rating (forging brass=100) 65
Hot working temperature 1400-1600 F or 750-875 C
Annealing temperature 800-1200 F or 425-650 C
Machinability rating (Free Cutting Brass=100) 85
Suitability for being joined by: Soldering/Excellent
Brazing/Good
Oxyacetylene Welding/Fair
Gas Shielded Arc Welding/Fair
Coated Metal Arc Welding/Not Recommended
Resistance Welding Spot/Not Recommended
Seam/Not Recommended
Butt/Fair
The values listed above represent reasonable approximations suitable for general engineering use. Due to commercial variations in composition and to manufacturing limitations, they should not be used for specification purposes. See applicable A.S.T.M. specification references.

C14500, C14500 Tellurium Copper, C10100 Copper, Copper C11000, C360 Brass, 932 Bronze, C95500, Astm B584, C83600, C95800, C36000, C93200, C93200 Bronze, Uns C14500, Naval Brass, C71500, Leaded Bronze, Astm B75, Bronze Rod, Copper And Copper Alloys Related words : C14500, C14500 Tellurium Copper, C10100 Copper, Copper C11000, C360 Brass, 932 Bronze, C95500, Astm B584, C83600, C95800, C36000, C93200, C93200 Bronze, Uns C14500, Naval Brass, C71500, Leaded Bronze, Astm B75, Bronze Rod, Copper And Copper Alloys
Please contact us for all your needs of

C14500 Tellurium Copper

at best prices from India. We are the biggest foundry casting alloy indian manufacturers exporters foundries in Jamnagar of

C14500 Tellurium Copper


C51000 Phosphor Bronze C51000 Phosphor Bronze C54400 Phosphor Bronze C54400 Phosphor Bronze
 Designed & maintained by:  www.conextechno.com 
Home | About Us | Products | Resources | Email | Contact Us | Sitemap
                   +