Brass Copper Fittings (INDIA) Home Email Sitemap
Home About Us Products Resources Email Contact Us Sitemap
Copper Turned Parts | Copper Fittings | Copper Pressed Parts | Copper Casting | Bronze Fittings | Copper Washers | Copper Bronze Grounding Parts | Bronze Casting | Copper Electrical Components | Brass Electrical Components | Brass Turned Parts | Brass Fasteners | Brass Casting | Copper Casting Alloys | Brass Wires Rods Alloys | Brass Hardware Fittings | Brass Sanitary Pipe Fittings | Brass Hose Fittings | Stainless Steel Fittings | Brass Moulding Inserts | Copper Lugs Terminals
Copper Turned Parts
Copper Fittings
Copper Pressed Parts
Copper Casting
Bronze Fittings
Copper Washers
Copper Bronze Grounding Parts
Bronze Casting
Copper Electrical Components
Brass Electrical Components
Brass Turned Parts
Brass Fasteners
Brass Casting
Copper Casting Alloys
Brass Wires Rods Alloys
Brass Hardware Fittings
Brass Sanitary Pipe fittings
Brass Hose Fittings
Stainless Steel Fittings
Brass Moulding Inserts
Copper Lugs Terminals
              C64200 Silicon A1. Bronze

C64200 Silicon A1. Bronze   Copper Alloy No. C64200   C64200 Silicon A1. Bronze

Silicon Aluminum Bronze, ASTM B150 CDA 642

Chemical Composition % by weight
Element Nominal Minimum Maximum
Copper 91.2 Rem. Rem.
Lead - - .05
Iron - - .30
Tin - - .20
Zinc - - .50
Aluminum 7 6.3 7.6
Manganese - - .10
Silicon 1.8 1.5 2.2
Nickel (incl. Co) - - .25
Arsenic - - .15
Applications
Valve stems, gears, marine hardware, pole line hardware, bolts, nuts, valve bodies and components.
Common Fabrication Processes
Hot forming, forging, machining.
Mechanical Properties
Typical for 1-1/2" Rod Hard (10%) Temper
Hardness* Rockwell F Scales 90
Tensile Strength** KSI 93
Yield Strength ** KSI 60
Elongation** % in 2 inch 26
**Test values are nominal approximations and depend on specimen size and orientation.
Physical Properties
Thermal Conductivity BTU/ (sq ft-ft-hr-F) 26
Specific Heat BTU/lb/ºF @ 68F .09
Thermal Expansion Per °F from 68 F to 212 F .0000100
Density lb/cu in @ 68 F .278
Electrical Conductivity % IACS @ 68 F 8
Modulus of Elasticity KSI 16,000
*Volume basis
Fabrication Practices
Capacity for being cold worked Poor
Capacity for being hot formed Excellent
Hot forgeability rating (forging brass =100) 80
Suitability for being joined by: Soldering/Not Recommended
Brazing/Fair
Oxyacetylene Welding/Not Recommended
Gas Shielded Arc Welding/Fair
Coated Metal Arc Welding/Fair
Resistance Welding Spot/Fair
Seam/Fair
Butt/Fair
The values listed above represent reasonable approximations suitable for general engineering use. Due to commercial variations in composition and to manufacturing limitations, they should not be used for specification purposes. See applicable A.S.T.M. specification references.

Bronze Alloys, Bronze Wire, Aluminium Bronze, Silicon Bronze, Phosphor Bronze Wire, Tantalum Wire, Nickel Silver Alloy, Nickel Alloys, Copper Nickel Alloys, Brass Alloys, Metal Alloys, Copper Alloys, Nickel Wire, Lead Alloys, High Temperature Alloys, Refractory Metals, Beryllium Copper, Zinc Alloy, Aluminium Brass, Alloys Related words : Bronze Alloys, Bronze Wire, Aluminium Bronze, Silicon Bronze, Phosphor Bronze Wire, Tantalum Wire, Nickel Silver Alloy, Nickel Alloys, Copper Nickel Alloys, Brass Alloys, Metal Alloys, Copper Alloys, Nickel Wire, Lead Alloys, High Temperature Alloys, Refractory Metals, Beryllium Copper, Zinc Alloy, Aluminium Brass, Alloys
Please contact us for all your needs of

C64200 Silicon A1. Bronze

at best prices from India. We are the biggest foundry casting alloy indian manufacturers exporters foundries in Jamnagar of

C64200 Silicon A1. Bronze


C18200 Chromium Copper C18200 Chromium Copper C36000 Free-Cutting Brass C36000 Free-Cutting Brass
 Designed & maintained by:  www.conextechno.com 
Home | About Us | Products | Resources | Email | Contact Us | Sitemap
                   +