Brass Copper Fittings (INDIA) Home Email Sitemap
Home About Us Products Resources Email Contact Us Sitemap
Copper Turned Parts | Copper Fittings | Copper Pressed Parts | Copper Casting | Bronze Fittings | Copper Washers | Copper Bronze Grounding Parts | Bronze Casting | Copper Electrical Components | Brass Electrical Components | Brass Turned Parts | Brass Fasteners | Brass Casting | Copper Casting Alloys | Brass Wires Rods Alloys | Brass Hardware Fittings | Brass Sanitary Pipe Fittings | Brass Hose Fittings | Stainless Steel Fittings | Brass Moulding Inserts | Copper Lugs Terminals
Copper Turned Parts
Copper Fittings
Copper Pressed Parts
Copper Casting
Bronze Fittings
Copper Washers
Copper Bronze Grounding Parts
Bronze Casting
Copper Electrical Components
Brass Electrical Components
Brass Turned Parts
Brass Fasteners
Brass Casting
Copper Casting Alloys
Brass Wires Rods Alloys
Brass Hardware Fittings
Brass Sanitary Pipe fittings
Brass Hose Fittings
Stainless Steel Fittings
Brass Moulding Inserts
Copper Lugs Terminals
              C83600 Leaded Red Brass

C83600 Leaded Red Brass   Copper Alloy No. C83600   C83600 Leaded Red Brass

Leaded Red Brass Alloy , CDA 836 , SAE 40

Chemical Composition % by weight
Element Nominal Minimum Maximum
Aluminum - - .005
Antimony - - .25
Copper 85 84 86
Iron - - .30
Lead 5 4 6
Nickel - - 1
Phosphorus - - .05
Silicon - - .005
Sulfur - - .08
Tin 5 4 6
Zinc 5 4 6
Applications
Pump components, small gears, water impellers and housings, marine fittings, flanges, low pressure valves and fittings, pipe fittings, plumbing fixtures, ornamental fixtures
Mechanical Properties
M07 - As Continuous Cast
Hardness* Brinell Hardness (500 kg load) 60
Tensile Strength** KSI 36
Yield Strength ** KSI (0.5% Ext. under load) 19
Elongation** % in 2 inch 15
**Test values are nominal approximations and depend on specimen size and orientation.
Physical Properties
Thermal Conductivity BTU/ (sq ft-ft-hr-F) 41.1
Specific Heat BTU/lb/ºF @ 68F .09
Thermal Expansion Per °F from 68 F to 572 F .000010
Density lb/cu in @ 68 F .318
Electrical Conductivity* (Annealed) % IACS @ 68 F 15
Modulus of Elasticity KSI 13,500
*Volume basis
Fabrication Practices
Stress relieving temperature 500 F or 260 C
Time at temperature 1 hour per inch of section thickness
Responds to heat treatment No
Machinability rating (Free Cutting Brass=100) 84
Suitability for being joined by: Soldering/Excellent
Brazing/Good*
Oxyacetylene Welding/Not Recommended
Gas Shielded Arc Welding/Not Recommended
Coated Metal Arc Welding/Fair
*Since brazing is performed at temperatures within the hot-short range, strain must be avoided during the brazing and cooling of this alloy.

The values listed above represent reasonable approximations suitable for general engineering use. Due to commercial variations in composition and to manufacturing limitations, they should not be used for specification purposes. See applicable A.S.T.M. specification references.

C83600, C360 Brass, Brass Alloys, 932 Bronze, C10100 Copper, Copper C11000, C14500, C95500, Astm B584, C95800, C36000, C93200, Brass Ingots, Naval Brass, C93200 Bronze, Brass Forging, Brass Rod, Cda 360 Brass, Uns C83600, C71500 Related words : C83600, C360 Brass, Brass Alloys, 932 Bronze, C10100 Copper, Copper C11000, C14500, C95500, Astm B584, C95800, C36000, C93200, Brass Ingots, Naval Brass, C93200 Bronze, Brass Forging, Brass Rod, Cda 360 Brass, Uns C83600, C71500
Please contact us for all your needs of

C83600 Leaded Red Brass

at best prices from India. We are the biggest foundry casting alloy indian manufacturers exporters foundries in Jamnagar of

C83600 Leaded Red Brass


Back to Continuous Cast Copper Alloys Back to Continuous Cast Copper Alloys C92900 Leaded Nickel Tin Bronze C92900 Leaded Nickel Tin Bronze
 Designed & maintained by:  www.conextechno.com 
Home | About Us | Products | Resources | Email | Contact Us | Sitemap
                   +