Brass Copper Fittings (INDIA) Home Email Sitemap
Home About Us Products Resources Email Contact Us Sitemap
Copper Turned Parts | Copper Fittings | Copper Pressed Parts | Copper Casting | Bronze Fittings | Copper Washers | Copper Bronze Grounding Parts | Bronze Casting | Copper Electrical Components | Brass Electrical Components | Brass Turned Parts | Brass Fasteners | Brass Casting | Copper Casting Alloys | Brass Wires Rods Alloys | Brass Hardware Fittings | Brass Sanitary Pipe Fittings | Brass Hose Fittings | Stainless Steel Fittings | Brass Moulding Inserts | Copper Lugs Terminals
Copper Turned Parts
Copper Fittings
Copper Pressed Parts
Copper Casting
Bronze Fittings
Copper Washers
Copper Bronze Grounding Parts
Bronze Casting
Copper Electrical Components
Brass Electrical Components
Brass Turned Parts
Brass Fasteners
Brass Casting
Copper Casting Alloys
Brass Wires Rods Alloys
Brass Hardware Fittings
Brass Sanitary Pipe fittings
Brass Hose Fittings
Stainless Steel Fittings
Brass Moulding Inserts
Copper Lugs Terminals
              C86300 Manganese Bronze

C86300 Manganese Bronze   Copper Alloy No. C86300   C86300 Manganese Bronze

High Tensile Manganese Bronze , SAE 430B , CDA 863

Chemical Composition % by weight
Element Nominal Minimum Maximum
Aluminum 6 5 7.5
Copper 63 60 66
Iron 3 2 4
Lead - - .20
Manganese 3 2.5 5
Nickel - - 1
Tin - - .20
Zinc 25 22 28
Applications
Extra heavy duty high strength alloy for large valve stems, gears, cams, slow speed heavy load bearings, screw down nuts, hydraulic cylinder parts.
Mechanical Properties
M07 - As Continuous Cast
Hardness* Brinell Hardness (500 kg load) 225
Tensile Strength** KSI 110 min
Yield Strength ** KSI (0.5% Ext. under load) 62 min
Elongation** % in 2 inch 14
**Test values are nominal approximations and depend on specimen size and orientation.
Physical Properties
Thermal Conductivity BTU/ (sq ft-ft-hr-F) 20.5
Specific Heat BTU/lb/ºF @ 68F .09
Thermal Expansion Per °F from 68 F to 572 F .000012
Density lb/cu in @ 68 F .283
Electrical Conductivity* (Annealed) % IACS @ 68 F 8
Modulus of Elasticity KSI 14,200
*Volume basis
Fabrication Practices
Stress relieving temperature 500 F or 260 C
Time at temperature 1 hour per inch of section thickness
Responds to heat treatment No
Machinability rating (Free Cutting Brass=100) 20
Suitability for being joined by: Soldering/Poor
Brazing/Poor
Oxyacetylene Welding/Poor
Gas Shielded Arc Welding/Poor
Coated Metal Arc Welding/Good
The values listed above represent reasonable approximations suitable for general engineering use. Due to commercial variations in composition and to manufacturing limitations, they should not be used for specification purposes. See applicable A.S.T.M. specification references.

C86300 Manganese Bronze, Bronze Alloys, Bronze Properties, Bronze Ingots, Properties Of Bronze, Aluminium Bronze, Nickel Aluminum Bronze, Bronze Wire, Leaded Bronze, Bronze Rod, Manganese Metal, Silicon Bronze, Phosphor Bronze Wire, Bronze Phosphor, Everdur, Nickel Silver Alloy, Beryllium Copper Alloys, Brass Alloys, Tantalum Wire, Copper Nickel Alloys Related words : C86300 Manganese Bronze, Bronze Alloys, Bronze Properties, Bronze Ingots, Properties Of Bronze, Aluminium Bronze, Nickel Aluminum Bronze, Bronze Wire, Leaded Bronze, Bronze Rod, Manganese Metal, Silicon Bronze, Phosphor Bronze Wire, Bronze Phosphor, Everdur, Nickel Silver Alloy, Beryllium Copper Alloys, Brass Alloys, Tantalum Wire, Copper Nickel Alloys
Please contact us for all your needs of

C86300 Manganese Bronze

at best prices from India. We are the biggest foundry casting alloy indian manufacturers exporters foundries in Jamnagar of

C86300 Manganese Bronze


C92900 Leaded Nickel Tin Bronze C92900 Leaded Nickel Tin Bronze C93200 (SAE 660) Bearing Bronze C93200 (SAE 660) Bearing Bronze
 Designed & maintained by:  www.conextechno.com 
Home | About Us | Products | Resources | Email | Contact Us | Sitemap
                   +