Brass Copper Fittings (INDIA) Home Email Sitemap
Home About Us Products Resources Email Contact Us Sitemap
Copper Turned Parts | Copper Fittings | Copper Pressed Parts | Copper Casting | Bronze Fittings | Copper Washers | Copper Bronze Grounding Parts | Bronze Casting | Copper Electrical Components | Brass Electrical Components | Brass Turned Parts | Brass Fasteners | Brass Casting | Copper Casting Alloys | Brass Wires Rods Alloys | Brass Hardware Fittings | Brass Sanitary Pipe Fittings | Brass Hose Fittings | Stainless Steel Fittings | Brass Moulding Inserts | Copper Lugs Terminals
Copper Turned Parts
Copper Fittings
Copper Pressed Parts
Copper Casting
Bronze Fittings
Copper Washers
Copper Bronze Grounding Parts
Bronze Casting
Copper Electrical Components
Brass Electrical Components
Brass Turned Parts
Brass Fasteners
Brass Casting
Copper Casting Alloys
Brass Wires Rods Alloys
Brass Hardware Fittings
Brass Sanitary Pipe fittings
Brass Hose Fittings
Stainless Steel Fittings
Brass Moulding Inserts
Copper Lugs Terminals
              C94100 High Leaded Tin Bronze

C94100 High leaded Tin Bronze   Copper Alloy No. C94100   C94100 High leaded Tin Bronze

High Leaded Tin Bronze SAE 94 , CDA 941

ASTM B 505
Chemical Composition % by weight
Element Nominal Minimum Maximum
Aluminum - - .005
Copper 75.5 72 79
Iron - - .25
Lead 20 18 22
Nickel - - 1
Phosphorus - - .05
Silicon - - .005
Sulfur - - .08
Tin 5.5 4.5 6.5
Zinc - - 1
Applications
High speed bearings for light loads.
Mechanical Properties
M07 - As Continuous Cast
Hardness* Brinell Hardness (500 kg load) 52
Tensile Strength** KSI 25
Yield Strength ** KSI (0.5% Ext. under load) 17
Elongation** % in 2 inch 16
**Test values are nominal approximations and depend on specimen size and orientation.
Physical Properties
Thermal Conductivity BTU/ (sq ft-ft-hr-F) 36.2
Specific Heat BTU/lb/ºF @ 68F .09
Thermal Expansion Per °F from 68 F to 572 F N/A
Density lb/cu in @ 68 F .336
Electrical Conductivity* (Annealed) % IACS @ 68 F 9
Modulus of Elasticity KSI 10,500
*Volume basis
Fabrication Practices
Stress relieving temperature 500 F or 260 C
Time at temperature 1 hour per inch of section thickness
Responds to heat treatment No
Machinability rating (Free Cutting Brass=100) 75
Suitability for being joined by: Soldering/Good
Brazing/Poor*
Oxyacetylene Welding/Not Recommended
Gas Shielded Arc Welding/Not Recommended
Coated Metal Arc Welding/Not Recommended
*Since brazing is performed at temperatures within the hot-short range, strain must be avoided during the brazing and cooling of this alloy.

The values listed above represent reasonable approximations suitable for general engineering use. Due to commercial variations in composition and to manufacturing limitations, they should not be used for specification purposes. See applicable A.S.T.M. specification references.

Bronze Alloys, Bronze Properties, Tin Bronze, Lead Alloys, Bronze Wire, High Temperature Alloys, Aluminium Bronze, Nickel Aluminum Bronze, Bronze Rod, Phosphor Bronze Wire, Silicon Bronze, Beryllium Copper Alloys, Nickel Silver Alloy, Tantalum Wire, Brass Alloys, Nickel Alloys, Copper Nickel Alloys, Metal Alloys, Nickel Wire, Copper Alloys Related words : Bronze Alloys, Bronze Properties, Tin Bronze, Lead Alloys, Bronze Wire, High Temperature Alloys, Aluminium Bronze, Nickel Aluminum Bronze, Bronze Rod, Phosphor Bronze Wire, Silicon Bronze, Beryllium Copper Alloys, Nickel Silver Alloy, Tantalum Wire, Brass Alloys, Nickel Alloys, Copper Nickel Alloys, Metal Alloys, Nickel Wire, Copper Alloys
Please contact us for all your needs of

C94100 High Leaded Tin Bronze

at best prices from India. We are the biggest foundry casting alloy indian manufacturers exporters foundries in Jamnagar of

C94100 High Leaded Tin Bronze


C90700 Tin Bronze C90700 Tin Bronze C91000 Tin Bronze C91000 Tin Bronze
 Designed & maintained by:  www.conextechno.com 
Home | About Us | Products | Resources | Email | Contact Us | Sitemap
                   +