Brass Copper Fittings (INDIA) Home Email Sitemap
Home About Us Products Resources Email Contact Us Sitemap
Copper Turned Parts | Copper Fittings | Copper Pressed Parts | Copper Casting | Bronze Fittings | Copper Washers | Copper Bronze Grounding Parts | Bronze Casting | Copper Electrical Components | Brass Electrical Components | Brass Turned Parts | Brass Fasteners | Brass Casting | Copper Casting Alloys | Brass Wires Rods Alloys | Brass Hardware Fittings | Brass Sanitary Pipe Fittings | Brass Hose Fittings | Stainless Steel Fittings | Brass Moulding Inserts | Copper Lugs Terminals
Copper Turned Parts
Copper Fittings
Copper Pressed Parts
Copper Casting
Bronze Fittings
Copper Washers
Copper Bronze Grounding Parts
Bronze Casting
Copper Electrical Components
Brass Electrical Components
Brass Turned Parts
Brass Fasteners
Brass Casting
Copper Casting Alloys
Brass Wires Rods Alloys
Brass Hardware Fittings
Brass Sanitary Pipe fittings
Brass Hose Fittings
Stainless Steel Fittings
Brass Moulding Inserts
Copper Lugs Terminals
              C97600 Nickel Silver Bronze

C97600 Nickel Silver Bronze   Copper Alloy No. C97600   C97600 Nickel Silver Bronze

Nickel Silver CDA 976 , Dairy Metal , 20% Leaded Nickel Silver

ASTM B 505 , ASTM B 271
Chemical Composition % by weight
Element Nominal Minimum Maximum
Aluminum - - .005
Antimony - - .25
Copper 65 63 67
Iron - - 1.5
Lead 4 3 5
Manganese - - 1
Nickel 20.3 19 21.5
Phosphorus - - .05
Silicon - - .15
Sulfur - - .08
Tin 4 3.5 4.5
Zinc 6 3 9
Applications
Marine castings, sanitary fittings, ornamental hardware, valves and pumps.
Mechanical Properties
M07 - As Continuous Cast
Hardness* Brinell Hardness (500 kg load) 80
Tensile Strength** KSI 45
Yield Strength ** KSI (0.5% Ext. under load) 24
Elongation** % in 2 inch 20
**Test values are nominal approximations and depend on specimen size and orientation.
Physical Properties
Thermal Conductivity BTU/ (sq ft-ft-hr-F) 13
Specific Heat BTU/lb/ºF @ 68F .09
Thermal Expansion Per °F from 68 F to 572 F .0000093
Density lb/cu in @ 68 F .321
Electrical Conductivity* (Annealed) % IACS @ 68 F 5
Modulus of Elasticity KSI 19,000
*Volume basis
Fabrication Practices
Stress relieving temperature 500 F or 260 C
Time at temperature 1 hour per inch of section thickness
Responds to heat treatment No
Machinability rating (Free Cutting Brass=100) 70
Suitability for being joined by: Soldering/Excellent
Brazing/Excellent
Oxyacetylene Welding/Not Recommended
Carbon Arc Welding/Not Recommended
Gas Shielded Arc Welding/Not Recommended
Coated Metal Arc Welding/Not Recommended
*Since brazing is performed at temperatures within the hot-short range, strain must be avoided during the brazing and cooling of this alloy.

The values listed above represent reasonable approximations suitable for general engineering use. Due to commercial variations in composition and to manufacturing limitations, they should not be used for specification purposes. See applicable A.S.T.M. specification references.

Bronze Alloys, Bronze Properties, Nickel Alloys, Nickel Wire, Nickel Silver Alloy, Nickel Aluminum Bronze, Bronze Wire, Copper Nickel Alloys, Aluminium Bronze, Nickel Metals, Bronze Rod, Silicon Bronze, Phosphor Bronze Wire, Bronze Phosphor, Tantalum Rod, Beryllium Copper Alloys, Brass Alloys, Tantalum Wire, Copper Alloys, Metal Alloys Related words : Bronze Alloys, Bronze Properties, Nickel Alloys, Nickel Wire, Nickel Silver Alloy, Nickel Aluminum Bronze, Bronze Wire, Copper Nickel Alloys, Aluminium Bronze, Nickel Metals, Bronze Rod, Silicon Bronze, Phosphor Bronze Wire, Bronze Phosphor, Tantalum Rod, Beryllium Copper Alloys, Brass Alloys, Tantalum Wire, Copper Alloys, Metal Alloys
Please contact us for all your needs of

C97600 Nickel Silver Bronze

at best prices from India. We are the biggest foundry casting alloy indian manufacturers exporters foundries in Jamnagar of

C97600 Nickel Silver Bronze


C92700 Leaded Tin Bronze C92700 Leaded Tin Bronze C92800 Leaded Tin Bronze C92800 Leaded Tin Bronze
 Designed & maintained by:  www.conextechno.com 
Home | About Us | Products | Resources | Email | Contact Us | Sitemap
                   +