Brass Copper Fittings (INDIA) Home Email Sitemap
Home About Us Products Resources Email Contact Us Sitemap
Copper Turned Parts | Copper Fittings | Copper Pressed Parts | Copper Casting | Bronze Fittings | Copper Washers | Copper Bronze Grounding Parts | Bronze Casting | Copper Electrical Components | Brass Electrical Components | Brass Turned Parts | Brass Fasteners | Brass Casting | Copper Casting Alloys | Brass Wires Rods Alloys | Brass Hardware Fittings | Brass Sanitary Pipe Fittings | Brass Hose Fittings | Stainless Steel Fittings | Brass Moulding Inserts | Copper Lugs Terminals
Copper Turned Parts
Copper Fittings
Copper Pressed Parts
Copper Casting
Bronze Fittings
Copper Washers
Copper Bronze Grounding Parts
Bronze Casting
Copper Electrical Components
Brass Electrical Components
Brass Turned Parts
Brass Fasteners
Brass Casting
Copper Casting Alloys
Brass Wires Rods Alloys
Brass Hardware Fittings
Brass Sanitary Pipe fittings
Brass Hose Fittings
Stainless Steel Fittings
Brass Moulding Inserts
Copper Lugs Terminals
              Free-Machining Brass C36000

Free-Machining Brass C36000   Copper Alloy No. C36000   Free-Machining Brass C36000

Free Cutting Brass , ASTM B16 CDA 360

Chemical Composition % by weight
Copper Lead Iron Zinc
61.5 Nominal 2.5 Min .35 Max 35.4 Nominal
Applications
Hardware : Fuse Gears and pinions.
Industrial : Automatic high speed screw machine parts.
Mechanical Properties
Typical for 1" rod half hard temper (20%)
Hardness* Rockwell F Scales 78
Tensile Strength** KSI 58
Yield Strength ** KSI 45
Elongation** % in 2 inch 25
**Test values are nominal approximations and depend on specimen size and orientation.
Physical Properties
Thermal Conductivity BTU/ (sq ft-ft-hr-F) 67
Specific Heat BTU/lb/ºF @ 68F .09
Thermal Expansion Per °F from 68 F to 212 F .0000114
Density lb/cu in @ 68 F .307
Electrical Conductivity % IACS @ 68 F 26
Modulus of Elasticity KSI 14,000
*Volume basis
Fabrication Practices
Capacity for being cold worked Poor
Capacity for being hot formed Fair
Hot forgeability rating (forging brass =100) N/A
Hot working temperature 1300-1450 F or 700-800 C
Annealing temperature 800-1100 F or 425-600 C
Machinability rating (Free Cutting Brass=100) 100
Suitability for being joined by: Soldering/Excellent
Brazing/Good
Oxyacetylene Welding/Not Recommended
Gas Shielded Arc Welding/Not Recommended
Coated Metal Arc Welding/Not Recommended
Resistance Welding Spot/Not Recommended
Seam/Not Recommended
Butt/Fair
The values listed above represent reasonable approximations suitable for general engineering use. Due to commercial variations in composition and to manufacturing limitations, they should not be used for specification purposes. See applicable A.S.T.M. specification references.

C36000, Brass Machining, Brass C36000, C360 Brass, Brass Alloys, C10100 Copper, 932 Bronze, Copper C11000, C14500, C95500, Astm B584, C83600, C95800, C93200, Naval Brass, Oxygen Free Copper, C93200 Bronze, Brass Forging, Brass Rod, Cda 360 Brass Related words : C36000, Brass Machining, Brass C36000, C360 Brass, Brass Alloys, C10100 Copper, 932 Bronze, Copper C11000, C14500, C95500, Astm B584, C83600, C95800, C93200, Naval Brass, Oxygen Free Copper, C93200 Bronze, Brass Forging, Brass Rod, Cda 360 Brass
Please contact us for all your needs of

Free-Machining Brass C36000

at best prices from India. We are the biggest foundry casting alloy indian manufacturers exporters foundries in Jamnagar of

Free-Machining Brass C36000


Beryllium Copper C17510 Class III Beryllium Copper C17510 Class III Lead-Free Naval Brass C46400 Lead-Free Naval Brass C46400
 Designed & maintained by:  www.conextechno.com 
Home | About Us | Products | Resources | Email | Contact Us | Sitemap
                   +