Brass Copper Fittings (INDIA) Home Email Sitemap
Home About Us Products Resources Email Contact Us Sitemap
Copper Turned Parts | Copper Fittings | Copper Pressed Parts | Copper Casting | Bronze Fittings | Copper Washers | Copper Bronze Grounding Parts | Bronze Casting | Copper Electrical Components | Brass Electrical Components | Brass Turned Parts | Brass Fasteners | Brass Casting | Copper Casting Alloys | Brass Wires Rods Alloys | Brass Hardware Fittings | Brass Sanitary Pipe Fittings | Brass Hose Fittings | Stainless Steel Fittings | Brass Moulding Inserts | Copper Lugs Terminals
Copper Turned Parts
Copper Fittings
Copper Pressed Parts
Copper Casting
Bronze Fittings
Copper Washers
Copper Bronze Grounding Parts
Bronze Casting
Copper Electrical Components
Brass Electrical Components
Brass Turned Parts
Brass Fasteners
Brass Casting
Copper Casting Alloys
Brass Wires Rods Alloys
Brass Hardware Fittings
Brass Sanitary Pipe fittings
Brass Hose Fittings
Stainless Steel Fittings
Brass Moulding Inserts
Copper Lugs Terminals
              Nickel Aluminum Bronze C95500

Nickel Aluminum Bronze C95500   Copper Alloy No. C95500   Nickel Aluminum Bronze C95500

Aluminum Bronze 9D, CDA 955 Nickel Aluminum Bronze , Grade D

ASTM B 505 , ASTM B 271
Chemical Composition % by weight
Element Nominal Minimum Maximum
Aluminum 11 10 11.5
Copper 81 78 -
Iron 4 3 5
Manganese - - 3.5
Nickel 4 3 5.5
Applications
Valve guides and seats in aircraft engines, corrosion resistant parts, bearings, bushings, gears, worm gears, pickling hooks and baskets, agitators.
Mechanical Properties (as cast)
M07 - As Continuous Cast
Hardness* Brinell Hardness (3000 kg load) 190
Tensile Strength** KSI 95 min
Yield Strength** KSI (0.5% Ext. under load) 42 min
Elongation** % in 2 inch 10
**Test values are nominal approximations and depend on specimen size and orientation.
Physical Properties
Thermal Conductivity BTU/ (sq ft-ft-hr-F) 24.2
Specific Heat BTU/lb/ºF @ 68F .10
Thermal Expansion Per °F from 68 F to 572 F .000009
Density lb/cu in @ 68 F .272
Electrical Conductivity* (Annealed) % IACS @ 68 F 8.5
Modulus of Elasticity KSI 16,000
*Volume basis
Fabrication Practices
Stress relieving temperature 600 F or 316 C
Time at temperature 1 hour per inch of section thickness
Responds to heat treatment Yes
Solution heat treating temperature 1585-1635 F or 860-890 C
Time at temperature 1 hour per inch of section thickness
Quenching medium Water or oil quench
Annealing temperature 1150-1225 F or 620-660 C
Time at temperature 1 hour per inch of section thickness
Machinability rating (Free Cutting Brass=100) 50
Suitability for being joined by: Soldering/Good
Brazing/Fair
Oxyacetylene Welding/Not Recommended
Carbon Arc Welding/Poor
Gas Shielded Arc Welding/Good
Coated Metal Arc Welding/Good
The values listed above represent reasonable approximations suitable for general engineering use. Due to commercial variations in composition and to manufacturing limitations, they should not be used for specification purposes. See applicable A.S.T.M. specification references.

C95500, 932 Bronze, Bronze Alloys, C360 Brass, C10100 Copper, Copper C11000, C14500, Astm B584, C83600, C95800, C36000, C93200 Bronze, C93200, Leaded Bronze, Bronze Rod, Phosphor Bronze, Phosphorous Bronze, C95400 Aluminum Bronze, Naval Brass, Uns C95500 Related words : C95500, 932 Bronze, Bronze Alloys, C360 Brass, C10100 Copper, Copper C11000, C14500, Astm B584, C83600, C95800, C36000, C93200 Bronze, C93200, Leaded Bronze, Bronze Rod, Phosphor Bronze, Phosphorous Bronze, C95400 Aluminum Bronze, Naval Brass, Uns C95500
Please contact us for all your needs of

Nickel Aluminum Bronze C95500

at best prices from India. We are the biggest foundry casting alloy indian manufacturers exporters foundries in Jamnagar of

Nickel Aluminum Bronze C95500


Manganese Bronze·C86300 Manganese Bronze·C86300 Tin Bronze Alloy C90300 Navy G Tin Bronze Alloy C90300 Navy G
 Designed & maintained by:  www.conextechno.com 
Home | About Us | Products | Resources | Email | Contact Us | Sitemap
                   +