Brass Copper Fittings (INDIA) Home Email Sitemap
Home About Us Products Resources Email Contact Us Sitemap
Copper Turned Parts | Copper Fittings | Copper Pressed Parts | Copper Casting | Bronze Fittings | Copper Washers | Copper Bronze Grounding Parts | Bronze Casting | Copper Electrical Components | Brass Electrical Components | Brass Turned Parts | Brass Fasteners | Brass Casting | Copper Casting Alloys | Brass Wires Rods Alloys | Brass Hardware Fittings | Brass Sanitary Pipe Fittings | Brass Hose Fittings | Stainless Steel Fittings | Brass Moulding Inserts | Copper Lugs Terminals
Copper Turned Parts
Copper Fittings
Copper Pressed Parts
Copper Casting
Bronze Fittings
Copper Washers
Copper Bronze Grounding Parts
Bronze Casting
Copper Electrical Components
Brass Electrical Components
Brass Turned Parts
Brass Fasteners
Brass Casting
Copper Casting Alloys
Brass Wires Rods Alloys
Brass Hardware Fittings
Brass Sanitary Pipe fittings
Brass Hose Fittings
Stainless Steel Fittings
Brass Moulding Inserts
Copper Lugs Terminals
              Oxygen-Free Copper C10100

Oxygen-Free Copper C10100   Copper No. C10100   Oxygen-Free Copper C10100

Oxygen Free High Conductivity Copper

UNS CDA 101 , ASTM B 187 , ASTM B 152
Nominal Chemical Composition % by weight
Copper Residual Deoxidants Phosphorus Tellurium
99.99 - .0003 max .0010 max
Material Properties
High thermal and electrical conductivity and high ductility combined with low volatility makes this material indispensable in the electronics industry.
Applications
Some typical uses for Copper Alloy 10100 in the electrical and electronic industries are bus bars, bus conductors, wave guides, hollow conductors, lead-in wires and anodes for vacuum tubes, glass to metal seals and others.
Mechanical Properties
Typical for 1" solid diameter Hard (35%) Temper
Hardness* Rockwell F Scales 87
Tensile Strength** KSI 48
Yield Strength ** KSI 55
Elongation** % in 2 inch 16
*Hardness conversions are approximate

**Test values are nominal approximations and depend on specimen size and orientation.
Physical Properties
Thermal Conductivity BTU/ (sq ft-ft-hr-F) 226
Specific Heat BTU/lb/ºF @ 68F .092
Thermal Expansion Per °F from 68 F to 212 F .0000094
Density lb/cu in @ 68 F .323
Electrical Conductivity % IACS @ 68 F 101
Modulus of Elasticity KSI 17,000
*Volume basis
Fabrication Practices
Capacity for being cold worked Excellent
Capacity for being hot formed Excellent
Hot forgeability rating (forging brass=100) 65
Hot working temperature 1400-1600 F or 750-875 C
Annealing temperature 700-1200 F or 375-650 C
Machinability rating (Free Cutting Brass=100) 20
Suitability for being joined by: Soldering/Excellent
Brazing/Good
Oxyacetylene Welding/Not Recommended
Gas Shielded Arc Welding/Fair
Coated Metal Arc Welding/Not Recommended
Resistance Welding Spot/Not Recommended
Seam/Not Recommended
Butt/Good
The values listed above represent reasonable approximations suitable for general engineering use. Due to commercial variations in composition and to manufacturing limitations, they should not be used for specification purposes. See applicable A.S.T.M. specification references.

C10100 Copper, C10100, C360 Brass, 932 Bronze, Copper C11000, C14500, C95500, Astm B584, C83600, C36000, C95800, C93200, Copper Alloys, Oxygen Free Copper, C93200 Bronze, Naval Brass, Uns C10100, Leaded Bronze, C71500, Astm B75 Related words : C10100 Copper, C10100, C360 Brass, 932 Bronze, Copper C11000, C14500, C95500, Astm B584, C83600, C36000, C95800, C93200, Copper Alloys, Oxygen Free Copper, C93200 Bronze, Naval Brass, Uns C10100, Leaded Bronze, C71500, Astm B75
Please contact us for all your needs of

Oxygen-Free Copper C10100

at best prices from India. We are the biggest foundry casting alloy indian manufacturers exporters foundries in Jamnagar of

Oxygen-Free Copper C10100


back to Wrought Copper Alloy Bar & Plate Back to Wrought Copper Alloy Bar & Plate Chrome Copper C18200 Class II Chrome Copper C18200 Class II
 Designed & maintained by:  www.conextechno.com 
Home | About Us | Products | Resources | Email | Contact Us | Sitemap
                   +