M07/TF00 As Continuous Cast, Solution and Precipitation Heat Treated
Hardness*
Brinell Hardness (500 kg load)
180
Tensile Strength**
KSI
75 min
Yield Strength **
KSI (0.5% Ext. under load)
50 min
Elongation**
% in 2 inch
5 min
**Test values are nominal approximations and depend on specimen size and orientation.
Physical Properties
Thermal Conductivity
BTU/ (sq ft-ft-hr-F)
31.2
Specific Heat
BTU/lb/ºF @ 68F
.09
Thermal Expansion
Per °F from 68 F to 572 F
.000011
Density
lb/cu in @ 68 F
.320
Electrical Conductivity* (Annealed)
% IACS @ 68 F
15
Modulus of Elasticity
KSI
15,000
*Volume basis
Fabrication Practices
Stress relieving temperature
500 F or 260 C
Time at temperature
1 hour per inch of section thickness
Responds to heat treatment
Yes
Solution heat treating temperature
1425-1475 F or 775-800 C
Time at temperature
2 hours per inch of section thickness
Quenching medium
Water
Precipitation hardening temperature
580-620 F or 305-325 C
Time at temperature
5 hours
Quenching medium
Air
Machinability rating (Free Cutting Brass=100)
30
Suitability for being joined by:
Soldering/Excellent
Brazing/Excellent*
Oxyacetylene Welding/Fair
Carbon Arc Welding/Not Recommended
Gas Shielded Arc Welding/Good
Coated Metal Arc Welding/Good
*Since brazing is performed at temperatures within the hot-short range, strain must be avoided during the brazing and cooling of this alloy.
The values listed above represent reasonable approximations suitable for general engineering use. Due to commercial variations in composition and to manufacturing limitations, they should not be used for specification purposes. See applicable A.S.T.M. specification references.