Brass Copper Fittings (INDIA) Home Email Sitemap
Home About Us Products Resources Email Contact Us Sitemap
Copper Turned Parts | Copper Fittings | Copper Pressed Parts | Copper Casting | Bronze Fittings | Copper Washers | Copper Bronze Grounding Parts | Bronze Casting | Copper Electrical Components | Brass Electrical Components | Brass Turned Parts | Brass Fasteners | Brass Casting | Copper Casting Alloys | Brass Wires Rods Alloys | Brass Hardware Fittings | Brass Sanitary Pipe Fittings | Brass Hose Fittings | Stainless Steel Fittings | Brass Moulding Inserts | Copper Lugs Terminals
Copper Turned Parts
Copper Fittings
Copper Pressed Parts
Copper Casting
Bronze Fittings
Copper Washers
Copper Bronze Grounding Parts
Bronze Casting
Copper Electrical Components
Brass Electrical Components
Brass Turned Parts
Brass Fasteners
Brass Casting
Copper Casting Alloys
Brass Wires Rods Alloys
Brass Hardware Fittings
Brass Sanitary Pipe fittings
Brass Hose Fittings
Stainless Steel Fittings
Brass Moulding Inserts
Copper Lugs Terminals
              C11000 Electrolytic Copper

C11000  Electrolytic Copper   Copper Alloy No. C11000   C11000  Electrolytic Copper

Electrolytic Tough Pitch Copper

CDA 110 ETP Copper , ASTM B 187 , ASTM B 152
Nominal Chemical Composition % by weight
Copper Oxygen
99.90 .04
Material Properties
Hard drawn bus bar with high thermal and electrical conductivity. Good resistance and tampering. Not suitable for case hardening.
Applications
Copper No. 11000 is used for welding fixtures, anodes, bus bar in electrical power installations, ground straps, commutators, etc. Its inherent fabrication qualities readily permit it to be bent, soldered, drilled, peened, riveted and formed to fit almost any design specification.
Mechanical Properties
Typical for 1" solid diameter Hard (35%) Temper
Hardness* Rockwell F Scales 87
Tensile Strength** KSI 48
Yield Strength ** KSI 44
Elongation** % in 2 inch 10
*Hardness conversions are approximate

**Test values are nominal approximations and depend on specimen size and orientation.
Physical Properties
Thermal Conductivity BTU/ (sq ft-ft-hr-F) 226
Specific Heat BTU/lb/ºF @ 68F .092
Thermal Expansion Per °F from 68 F to 212 F .0000094
Density lb/cu in @ 68 F .321-.323
Electrical Conductivity % IACS @ 68 F 101
Modulus of Elasticity KSI 17,000
*Volume basis
Fabrication Practices
Capacity for being cold worked Excellent
Capacity for being hot formed Excellent
Hot forgeability rating (forging brass=100) 65
Hot working temperature 1400-1600 F or 750-875 C
Annealing temperature 700-1200 F or 375-650 C
Machinability rating (Free Cutting Brass=100) 20
Suitability for being joined by: Soldering/Excellent
Brazing/Good
Oxyacetylene Welding/Not Recommended
Gas Shielded Arc Welding/Fair
Coated Metal Arc Welding/Not Recommended
Resistance Welding Spot/Not Recommended
Seam/Not Recommended
Butt/Good
The values listed above represent reasonable approximations suitable for general engineering use. Due to commercial variations in composition and to manufacturing limitations, they should not be used for specification purposes. See applicable A.S.T.M. specification references.

Copper C11000, C11000, C360 Brass, C10100 Copper, 932 Bronze, C14500, C95500, Astm B584, C83600, C36000, C95800, C93200, Copper Alloys, Oxygen Free Copper, C93200 Bronze, Uns C11000, Astm C11000, Naval Brass, Leaded Bronze, C71500 Related words : Copper C11000, C11000, C360 Brass, C10100 Copper, 932 Bronze, C14500, C95500, Astm B584, C83600, C36000, C95800, C93200, Copper Alloys, Oxygen Free Copper, C93200 Bronze, Uns C11000, Astm C11000, Naval Brass, Leaded Bronze, C71500
Please contact us for all your needs of

C11000 Electrolytic Copper

at best prices from India. We are the biggest foundry casting alloy indian manufacturers exporters foundries in Jamnagar of

C11000 Electrolytic Copper


Back to Other Wrought Copper Alloys Back to Other Wrought Copper Alloys C48500 Leaded Naval Brass C48500 Leaded Naval Brass
 Designed & maintained by:  www.conextechno.com 
Home | About Us | Products | Resources | Email | Contact Us | Sitemap
                   +