Brass Copper Fittings (INDIA) Home Email Sitemap
Home About Us Products Resources Email Contact Us Sitemap
Copper Turned Parts | Copper Fittings | Copper Pressed Parts | Copper Casting | Bronze Fittings | Copper Washers | Copper Bronze Grounding Parts | Bronze Casting | Copper Electrical Components | Brass Electrical Components | Brass Turned Parts | Brass Fasteners | Brass Casting | Copper Casting Alloys | Brass Wires Rods Alloys | Brass Hardware Fittings | Brass Sanitary Pipe Fittings | Brass Hose Fittings | Stainless Steel Fittings | Brass Moulding Inserts | Copper Lugs Terminals
Copper Turned Parts
Copper Fittings
Copper Pressed Parts
Copper Casting
Bronze Fittings
Copper Washers
Copper Bronze Grounding Parts
Bronze Casting
Copper Electrical Components
Brass Electrical Components
Brass Turned Parts
Brass Fasteners
Brass Casting
Copper Casting Alloys
Brass Wires Rods Alloys
Brass Hardware Fittings
Brass Sanitary Pipe fittings
Brass Hose Fittings
Stainless Steel Fittings
Brass Moulding Inserts
Copper Lugs Terminals
              C48500 Leaded Naval Brass

C48500 Leaded Naval Brass   Copper Alloy No. C48500   C48500 Leaded Naval Brass

Naval Brass , ASTM B21 CDA 485

Chemical Composition % by weight
Element Nominal Minimum Maximum
Copper 60 59 62
Lead 1.8 1.3 2.2
Lead - - .10
Tin .70 .50 1
Zinc 37.5 Remainder
Applications
Marine hardware, screw machine products, valve stems.
Common Fabrication Processes
Hot forging, pressing and machining.
Mechanical Properties
Typical for 1" Rod Half Hard (20%) Temper
Hardness* Rockwell F Scales 82
Tensile Strength** KSI 75
Yield Strength ** KSI 53
Elongation** % in 2 inch 15
**Test values are nominal approximations and depend on specimen size and orientation.
Physical Properties
Thermal Conductivity BTU/ (sq ft-ft-hr-F) 67
Specific Heat BTU/lb/ºF @ 68F .09
Thermal Expansion Per °F from 68 F to 212 F .0000118
Density lb/cu in @ 68 F .305
Electrical Conductivity % IACS @ 68 F 26
Modulus of Elasticity KSI 15,000
*Volume basis
Fabrication Practices
Capacity for being cold worked Poor
Capacity for being hot formed Good
Machinability rating (Free Cutting Brass=100) 70
Suitability for being joined by: Soldering/Excellent
Brazing/Good
Oxyacetylene Welding/Not Recommended
Gas Shielded Arc Welding/Not Recommended
Coated Metal Arc Welding/Not Recommended
Resistance Welding Spot/Not Recommended
Seam/Not Recommended
Butt/Fair
The values listed above represent reasonable approximations suitable for general engineering use. Due to commercial variations in composition and to manufacturing limitations, they should not be used for specification purposes. See applicable A.S.T.M. specification references.

Naval Brass, C360 Brass, Brass Alloys, C10100 Copper, 932 Bronze, Copper C11000, C14500, C95500, C11000, C83600, C36000, Astm B584, C95800, C93200, Ams 4640, C93200 Bronze,Brass Rod,Leaded Bronze, Cda 360 Brass, C71500 Related words : Naval Brass, C360 Brass, Brass Alloys, C10100 Copper, 932 Bronze, Copper C11000, C14500, C95500, C11000, C83600, C36000, Astm B584, C95800, C93200, Ams 4640, C93200 Bronze,Brass Rod,Leaded Bronze, Cda 360 Brass, C71500
Please contact us for all your needs of

C48500 Leaded Naval Brass

at best prices from India. We are the biggest foundry casting alloy indian manufacturers exporters foundries in Jamnagar of

C48500 Leaded Naval Brass


C11000  Electrolytic Copper C11000 Electrolytic Copper C10100 Oxygen-Free Copper C10100 Oxygen-Free Copper
 Designed & maintained by:  www.conextechno.com 
Home | About Us | Products | Resources | Email | Contact Us | Sitemap
                   +