Brass Copper Fittings (INDIA) Home Email Sitemap
Home About Us Products Resources Email Contact Us Sitemap
Copper Turned Parts | Copper Fittings | Copper Pressed Parts | Copper Casting | Bronze Fittings | Copper Washers | Copper Bronze Grounding Parts | Bronze Casting | Copper Electrical Components | Brass Electrical Components | Brass Turned Parts | Brass Fasteners | Brass Casting | Copper Casting Alloys | Brass Wires Rods Alloys | Brass Hardware Fittings | Brass Sanitary Pipe Fittings | Brass Hose Fittings | Stainless Steel Fittings | Brass Moulding Inserts | Copper Lugs Terminals
Copper Turned Parts
Copper Fittings
Copper Pressed Parts
Copper Casting
Bronze Fittings
Copper Washers
Copper Bronze Grounding Parts
Bronze Casting
Copper Electrical Components
Brass Electrical Components
Brass Turned Parts
Brass Fasteners
Brass Casting
Copper Casting Alloys
Brass Wires Rods Alloys
Brass Hardware Fittings
Brass Sanitary Pipe fittings
Brass Hose Fittings
Stainless Steel Fittings
Brass Moulding Inserts
Copper Lugs Terminals
              C46400 Lead Free Naval Brass

C46400 Lead Free Naval Brass   Copper Alloy No. C17510   C46400 Lead Free Naval Brass

Naval Brass , CDA 464

ASTM B21 , ASTM B171
Chemical Composition % by weight
Element Nominal Minimum Maximum
Copper 60 59 62
Lead - - .20
Iron - - .10
Tin .8 .5 1
Zinc 39.2 Remainder
Arsenic** - .02 .06
Sb or P** - .02 .10
* The uninhibited alloy is is copper alloy no. C46400.
** Arsenic, Antimony and Phosphorus inhibited alloys are identified respectively by copper alloy nos. C46500, C46600 and C46700.
Applications
Hardware : Aircraft turnbuckle barrels, balls, bolts.
Industrial : Condenser plates, welding rod.
Common Fabrication Processes
Blanking, drawing, forming and bending, heading and upsetting, hot forging and pressing, hot heading and upsetting, shearing.
Mechanical Properties
Typical for 1" Rod Half Hard (20%) Temper
Hardness* Rockwell F Scales 82
Tensile Strength** KSI 75
Yield Strength ** KSI 53
Elongation** % in 2 inch 20
**Test values are nominal approximations and depend on specimen size and orientation.
Physical Properties
Thermal Conductivity BTU/ (sq ft-ft-hr-F) 67
Specific Heat BTU/lb/ºF @ 68F .09
Thermal Expansion Per °F from 68 F to 212 F .0000118
Density lb/cu in @ 68 F .304
Electrical Conductivity % IACS @ 68 F 26
Modulus of Elasticity KSI 15,000
*Volume basis
Fabrication Practices
Capacity for being cold worked Fair
Capacity for being hot formed Excellent
Machinability rating (Free Cutting Brass=100) 30
Suitability for being joined by: Soldering/Excellent
Brazing/Excellent
Oxyacetylene Welding/Good
Gas Shielded Arc Welding/Fair
Coated Metal Arc Welding/Not Recommended
Resistance Welding Spot/Good
Seam/Fair
Butt/Good
The values listed above represent reasonable approximations suitable for general engineering use. Due to commercial variations in composition and to manufacturing limitations, they should not be used for specification purposes. See applicable A.S.T.M. specification references.

Naval Brass, Brass Alloys, Lead Alloys, Aluminium Brass, Brass Wire, C46400, C360 Brass, C83600, C10100 Copper, C11000, Copper C11000, C36000, C14500, C95500, Ams 4640, 932 Bronze, C93200, Astm B584, C95800, Leaded Bronze Related words : Naval Brass, Brass Alloys, Lead Alloys, Aluminium Brass, Brass Wire, C46400, C360 Brass, C83600, C10100 Copper, C11000, Copper C11000, C36000, C14500, C95500, Ams 4640, 932 Bronze, C93200, Astm B584, C95800, Leaded Bronze
Please contact us for all your needs of

C46400 Lead Free Naval Brass

at best prices from India. We are the biggest foundry casting alloy indian manufacturers exporters foundries in Jamnagar of

C46400 Lead Free Naval Brass


C67300 Manganese Bronze C67300 Manganese Bronze C67500 Manganese Bronze C67500 Manganese Bronze
 Designed & maintained by:  www.conextechno.com 
Home | About Us | Products | Resources | Email | Contact Us | Sitemap
                   +