Brass Copper Fittings (INDIA) Home Email Sitemap
Home About Us Products Resources Email Contact Us Sitemap
Copper Turned Parts | Copper Fittings | Copper Pressed Parts | Copper Casting | Bronze Fittings | Copper Washers | Copper Bronze Grounding Parts | Bronze Casting | Copper Electrical Components | Brass Electrical Components | Brass Turned Parts | Brass Fasteners | Brass Casting | Copper Casting Alloys | Brass Wires Rods Alloys | Brass Hardware Fittings | Brass Sanitary Pipe Fittings | Brass Hose Fittings | Stainless Steel Fittings | Brass Moulding Inserts | Copper Lugs Terminals
Copper Turned Parts
Copper Fittings
Copper Pressed Parts
Copper Casting
Bronze Fittings
Copper Washers
Copper Bronze Grounding Parts
Bronze Casting
Copper Electrical Components
Brass Electrical Components
Brass Turned Parts
Brass Fasteners
Brass Casting
Copper Casting Alloys
Brass Wires Rods Alloys
Brass Hardware Fittings
Brass Sanitary Pipe fittings
Brass Hose Fittings
Stainless Steel Fittings
Brass Moulding Inserts
Copper Lugs Terminals
              C67300 Manganese Bronze

C67300 Manganese Bronze   Copper Alloy No. C67300   C67300 Manganese Bronze

Manganese Silicon Bronze , CDA 673

Chemical Composition % by weight
Element Nominal Minimum Maximum
Copper 60.5 58 63
Lead 1.7 .40 3
Iron - - .50
Tin - - .50
Zinc Remainder
Nickel (incl. Co) - - .25
Aluminum - - .25
Manganese 2.75 2 3.5
Silicon 1 .5 1.5
Applications
Hydraulic piston shoes, cylinder liners, cams.
Common Fabrication Processes
Machining
Mechanical Properties
Typical for 2" Bar As Extruded Temper
Hardness* Rockwell F Scales 75
Tensile Strength** KSI 78
Yield Strength ** KSI 36
Elongation** % in 2 inch 26
**Test values are nominal approximations and depend on specimen size and orientation.
Physical Properties
Thermal Conductivity BTU/ (sq ft-ft-hr-F) 58
Specific Heat BTU/lb/ºF @ 68F .09
Thermal Expansion Per °F from 68 F to 212 F .000011
Density lb/cu in @ 68 F .293
Electrical Conductivity % IACS @ 68 F 23
Modulus of Elasticity KSI 16,000
*Volume basis
Fabrication Practices
Capacity for being cold worked Fair
Suitability for being joined by: Soldering/Good
Brazing/Not Recommended
Oxyacetylene Welding/Not Recommended
Gas Shielded Arc Welding/Fair
Coated Metal Arc Welding/Not Recommended
Resistance Welding Spot/Good
Seam/Good
Butt/Good
The values listed above represent reasonable approximations suitable for general engineering use. Due to commercial variations in composition and to manufacturing limitations, they should not be used for specification purposes. See applicable A.S.T.M. specification references.

Bronze Alloys, Bronze Properties, Bronze Ingots, Properties Of Bronze, Aluminium Bronze, Nickel Aluminum Bronze, Bronze Wire, Leaded Bronze, Bronze Rod, Manganese Metal, Silicon Bronze, Phosphor Bronze Wire, Bronze Phosphor, Everdur, Nickel Silver Alloy, Beryllium Copper Alloys, Brass Alloys, Tantalum Wire, Copper Nickel Alloys, Nickel Alloys Related words : Bronze Alloys, Bronze Properties, Bronze Ingots, Properties Of Bronze, Aluminium Bronze, Nickel Aluminum Bronze, Bronze Wire, Leaded Bronze, Bronze Rod, Manganese Metal, Silicon Bronze, Phosphor Bronze Wire, Bronze Phosphor, Everdur, Nickel Silver Alloy, Beryllium Copper Alloys, Brass Alloys, Tantalum Wire, Copper Nickel Alloys, Nickel Alloys
Please contact us for all your needs of

C67300 Manganese Bronze

at best prices from India. We are the biggest foundry casting alloy indian manufacturers exporters foundries in Jamnagar of

C67300 Manganese Bronze


C38500 Architectural Bronze C38500 Architectural Bronze C46400 Lead Free Naval Brass C46400 Lead Free Naval Brass
 Designed & maintained by:  www.conextechno.com 
Home | About Us | Products | Resources | Email | Contact Us | Sitemap
                   +