Blanking, drawing, forming and bending, heading and upsetting, hot forging and pressing, roll threading and knurling, shearing, squeezing and swaging.
Mechanical Properties
Typical for 1" Rod Hard (36%) Temper
Hardness*
Rockwell F Scales
92
Tensile Strength**
KSI
92
Yield Strength **
KSI
55
Elongation**
% in 2 inch
22
**Test values are nominal approximations and depend on specimen size and orientation.
Physical Properties
Thermal Conductivity
BTU/ (sq ft-ft-hr-F)
21
Specific Heat
BTU/lb/ºF @ 68F
.09
Thermal Expansion
Per °F from 68 F to 212 F
.0000100
Density
lb/cu in @ 68 F
.308
Electrical Conductivity
% IACS @ 68 F
7
Modulus of Elasticity
KSI
15,000
*Volume basis
Fabrication Practices
Capacity for being cold worked
Excellent
Capacity for being hot formed
Excellent
Hot forgeability rating (forging brass =100)
40
Suitability for being joined by:
Soldering/Good
Brazing/Excellent
Oxyacetylene Welding/Good
Gas Shielded Arc Welding/Excellent
Coated Metal Arc Welding/Fair
Resistance Welding
Spot/Excellent
Seam/Excellent
Butt/Excellent
The values listed above represent reasonable approximations suitable for general engineering use. Due to commercial variations in composition and to manufacturing limitations, they should not be used for specification purposes. See applicable A.S.T.M. specification references.