Brass Copper Fittings (INDIA) Home Email Sitemap
Home About Us Products Resources Email Contact Us Sitemap
Copper Turned Parts | Copper Fittings | Copper Pressed Parts | Copper Casting | Bronze Fittings | Copper Washers | Copper Bronze Grounding Parts | Bronze Casting | Copper Electrical Components | Brass Electrical Components | Brass Turned Parts | Brass Fasteners | Brass Casting | Copper Casting Alloys | Brass Wires Rods Alloys | Brass Hardware Fittings | Brass Sanitary Pipe Fittings | Brass Hose Fittings | Stainless Steel Fittings | Brass Moulding Inserts | Copper Lugs Terminals
Copper Turned Parts
Copper Fittings
Copper Pressed Parts
Copper Casting
Bronze Fittings
Copper Washers
Copper Bronze Grounding Parts
Bronze Casting
Copper Electrical Components
Brass Electrical Components
Brass Turned Parts
Brass Fasteners
Brass Casting
Copper Casting Alloys
Brass Wires Rods Alloys
Brass Hardware Fittings
Brass Sanitary Pipe fittings
Brass Hose Fittings
Stainless Steel Fittings
Brass Moulding Inserts
Copper Lugs Terminals
              C38500 Architectural Bronze

C38500 Architectural Bronze   Copper Alloy No. C38500   C38500 Architectural Bronze

Architectural Bronze, CDA 385

Chemical Composition % by weight
Element Nominal Minimum Maximum
Copper 57 55 59
Lead 3 2.5 3.5
Iron - - .35
Zinc 40 Rem. Rem.
Applications
Architectural extrusions, trim, butts, hinges, lock bodies.
Common Fabrication Processes
Hot forging and pressing, hot forming and bending, machining.
Mechanical Properties
Typical for 1" dia. rod as extruded
Hardness* Rockwell F Scales 65
Tensile Strength** KSI 60
Yield Strength ** KSI 20
Elongation** % in 2 inch 30
**Test values are nominal approximations and depend on specimen size and orientation.
Physical Properties
Thermal Conductivity BTU/ (sq ft-ft-hr-F) 71
Specific Heat BTU/lb/ºF @ 68F .09
Thermal Expansion Per °F from 68 F to 212 F .0000209
Density lb/cu in @ 68 F .306
Electrical Conductivity % IACS @ 68 F 28
Modulus of Elasticity KSI 5,300
*Volume basis
Fabrication Practices
Capacity for being cold worked Poor
Capacity for being hot formed Excellent
Hot forgeability rating (forging brass =100) -
Hot working temperature 1150-1350 F (625-725 C)  
Annealing temperature 800-1100 F (425-600 C)
Machinability rating (Free Cutting Brass=100) 90
Suitability for being joined by: Soldering/Excellent
Brazing/Good
Oxyacetylene Welding/Not Recommended
Gas Shielded Arc Welding/Not Recommended
Coated Metal Arc Welding/Not Recommended
Resistance Welding Spot/Not Recommended
Seam/Not Recommended
Butt/Fair
The values listed above represent reasonable approximations suitable for general engineering use. Due to commercial variations in composition and to manufacturing limitations, they should not be used for specification purposes. See applicable A.S.T.M. specification references.

Oil Rubbed Bronze, Bronze Cabinet Pulls, Satin Bronze, Chrome Bronze, Bronze Finish, Bronze Pewter, Bronze Towel Bar, Bronze Versus Brass, Bronze Vs Brass, Difference Between Bronze And Brass, Bronze Gifts, Bronze Hardware, 360 Brass, Bronze Cabinet Hardware, Aluminum Nickel Bronze, Brass Cabinet Pulls, Cast Bronze, Door Knocker, Brass Cabinet Knobs, Switchplate Related words : Oil Rubbed Bronze, Bronze Cabinet Pulls, Satin Bronze, Chrome Bronze, Bronze Finish, Bronze Pewter, Bronze Towel Bar, Bronze Versus Brass, Bronze Vs Brass, Difference Between Bronze And Brass, Bronze Gifts, Bronze Hardware, 360 Brass, Bronze Cabinet Hardware, Aluminum Nickel Bronze, Brass Cabinet Pulls, Cast Bronze, Door Knocker, Brass Cabinet Knobs, Switchplate
Please contact us for all your needs of

C38500 Architectural Bronze

at best prices from India. We are the biggest foundry casting alloy indian manufacturers exporters foundries in Jamnagar of

C38500 Architectural Bronze


C65500 High Silicon Bronze C65500 High Silicon Bronze C67300 Manganese Bronze C67300 Manganese Bronze
 Designed & maintained by:  www.conextechno.com 
Home | About Us | Products | Resources | Email | Contact Us | Sitemap
                   +