Brass Copper Fittings (INDIA) Home Email Sitemap
Home About Us Products Resources Email Contact Us Sitemap
Copper Turned Parts | Copper Fittings | Copper Pressed Parts | Copper Casting | Bronze Fittings | Copper Washers | Copper Bronze Grounding Parts | Bronze Casting | Copper Electrical Components | Brass Electrical Components | Brass Turned Parts | Brass Fasteners | Brass Casting | Copper Casting Alloys | Brass Wires Rods Alloys | Brass Hardware Fittings | Brass Sanitary Pipe Fittings | Brass Hose Fittings | Stainless Steel Fittings | Brass Moulding Inserts | Copper Lugs Terminals
Copper Turned Parts
Copper Fittings
Copper Pressed Parts
Copper Casting
Bronze Fittings
Copper Washers
Copper Bronze Grounding Parts
Bronze Casting
Copper Electrical Components
Brass Electrical Components
Brass Turned Parts
Brass Fasteners
Brass Casting
Copper Casting Alloys
Brass Wires Rods Alloys
Brass Hardware Fittings
Brass Sanitary Pipe fittings
Brass Hose Fittings
Stainless Steel Fittings
Brass Moulding Inserts
Copper Lugs Terminals
              Manganese Bronze C67500

Manganese Bronze C67500   Copper Alloy No. C67500   Manganese Bronze C67500

Manganese Bronze A , CDA 675

Chemical Composition % by weight
Element Nominal Minimum Maximum
Copper 58.5 57 60
Lead - - .20
Iron 1.4 .8 2
Tin 1 .8 2
Zinc 39 Remainder
Aluminum - - .25
Manganese .1 .05 .50
Applications
Automotive : Clutch disks, pump rods, shafting.
Hardware : balls, valve stems and bodies.
Common Fabrication Processes
Hot forging and pressing, hot heading and upsetting, machining.
Mechanical Properties
Typical for 1" Rod Half Hard (20%) Temper
Hardness* Rockwell F Scales 90
Tensile Strength** KSI 84
Yield Strength ** KSI 60
Elongation** % in 2 inch 19
**Test values are nominal approximations and depend on specimen size and orientation.
Physical Properties
Thermal Conductivity BTU/ (sq ft-ft-hr-F) 61
Specific Heat BTU/lb/ºF @ 68F .09
Thermal Expansion Per °F from 68 F to 212 F .0000118
Density lb/cu in @ 68 F .302
Electrical Conductivity % IACS @ 68 F 24
Modulus of Elasticity KSI 15,000
*Volume basis
Fabrication Practices
Capacity for being cold worked Excellent
Capacity for being hot formed Good
Hot forgeability rating (forging brass=100) -
Hot working temperature 1200-1625 F or 650-765 C
Machinability rating (Free Cutting Brass=100) -
Solution heat treating temperature 1675-1725 F or 900-950 C
Suitability for being joined by: Soldering/Good
Brazing/Good
Oxyacetylene Welding/Not Recommended
Gas Shielded Arc Welding/Fair
Coated Metal Arc Welding/Fair
Resistance Welding Spot/Good
Seam/Fair
Butt/Fair
The values listed above represent reasonable approximations suitable for general engineering use. Due to commercial variations in composition and to manufacturing limitations, they should not be used for specification purposes. See applicable A.S.T.M. specification references.

Bronze Alloys, Bronze Properties, Bronze Ingots, Properties Of Bronze, Aluminium Bronze, Nickel Aluminum Bronze, Bronze Wire, Leaded Bronze, Bronze Rod, Manganese Metal, Silicon Bronze, Phosphor Bronze Wire, Bronze Phosphor, Everdur, Nickel Silver Alloy, Beryllium Copper Alloys, Brass Alloys, Tantalum Wire, Copper Nickel Alloys, Nickel Alloys Related words : Bronze Alloys, Bronze Properties, Bronze Ingots, Properties Of Bronze, Aluminium Bronze, Nickel Aluminum Bronze, Bronze Wire, Leaded Bronze, Bronze Rod, Manganese Metal, Silicon Bronze, Phosphor Bronze Wire, Bronze Phosphor, Everdur, Nickel Silver Alloy, Beryllium Copper Alloys, Brass Alloys, Tantalum Wire, Copper Nickel Alloys, Nickel Alloys
Please contact us for all your needs of

Manganese Bronze C67500

at best prices from India. We are the biggest foundry casting alloy indian manufacturers exporters foundries in Jamnagar of

Manganese Bronze C67500


Manganese Bronze C67300 Manganese Bronze C67300 Copper-Nickel C70600 (90/10) Copper-Nickel C70600 (90/10)
 Designed & maintained by:  www.conextechno.com 
Home | About Us | Products | Resources | Email | Contact Us | Sitemap
                   +