Brass Copper Fittings (INDIA) Home Email Sitemap
Home About Us Products Resources Email Contact Us Sitemap
Copper Turned Parts | Copper Fittings | Copper Pressed Parts | Copper Casting | Bronze Fittings | Copper Washers | Copper Bronze Grounding Parts | Bronze Casting | Copper Electrical Components | Brass Electrical Components | Brass Turned Parts | Brass Fasteners | Brass Casting | Copper Casting Alloys | Brass Wires Rods Alloys | Brass Hardware Fittings | Brass Sanitary Pipe Fittings | Brass Hose Fittings | Stainless Steel Fittings | Brass Moulding Inserts | Copper Lugs Terminals
Copper Turned Parts
Copper Fittings
Copper Pressed Parts
Copper Casting
Bronze Fittings
Copper Washers
Copper Bronze Grounding Parts
Bronze Casting
Copper Electrical Components
Brass Electrical Components
Brass Turned Parts
Brass Fasteners
Brass Casting
Copper Casting Alloys
Brass Wires Rods Alloys
Brass Hardware Fittings
Brass Sanitary Pipe fittings
Brass Hose Fittings
Stainless Steel Fittings
Brass Moulding Inserts
Copper Lugs Terminals
              Nickel Aluminum Bronze C63000

Nickel Aluminum Bronze C63000   Copper Alloy No. C63000   Nickel Aluminum Bronze C63000

Nickel Aluminum Bronze

ASTM B 150 CDA 630 , ASTM B171
Chemical Composition % by weight
Element Nominal Minimum Maximum
Copper 92 Rem. Rem.
Iron 3 2 5
Tin - - .20
Zinc - - .30
Aluminum 10 9 11
Manganese - - 1.5
Phosphorus - - .25
Nickel (incl. Co) 5 4 5.5
Applications
Nuts, bolts, valve seats, plunger tips, marine shafts, valve guides, aircraft parts, pump shafts, structural members.
Common Fabrication Processes
Hot forming, forging, machining.
Mechanical Properties
Typical for 1" Rod Half Hard (10%) Temper
Hardness* Rockwell F Scales 98
Tensile Strength** KSI 118
Yield Strength ** KSI 75
Elongation** % in 2 inch 15
**Test values are nominal approximations and depend on specimen size and orientation.
Physical Properties
Thermal Conductivity BTU/ (sq ft-ft-hr-F) 22.6
Specific Heat BTU/lb/ºF @ 68F .09
Thermal Expansion Per °F from 68 F to 212 F .0000090
Density lb/cu in @ 68 F .274
Electrical Conductivity % IACS @ 68 F 7
Modulus of Elasticity KSI 17,500
*Volume basis
Fabrication Practices
Capacity for being cold worked Poor
Capacity for being hot formed Good
Machinability Rating (Free Cutting Brass=100) 30
Suitability for being joined by: Soldering/Not Recommended
Brazing/Fair
Oxyacetylene Welding/Not Recommended
Gas Shielded Arc Welding/Good
Coated Metal Arc Welding/Good
Resistance Welding Spot/Good
Seam/Good
Butt/Good
The values listed above represent reasonable approximations suitable for general engineering use. Due to commercial variations in composition and to manufacturing limitations, they should not be used for specification purposes. See applicable A.S.T.M. specification references.

C63000, 932 Bronze, Bronze Alloys, C360 Brass, C10100 Copper, Copper C11000, C14500, C95500, Astm B584, C95800, C83600, C36000, C93200 Bronze, C93200, Leaded Bronze, Bronze Rod, Phosphor Bronze, C95400 Aluminum Bronze, Phosphorous Bronze, Uns C63000 Related words : C63000, 932 Bronze, Bronze Alloys, C360 Brass, C10100 Copper, Copper C11000, C14500, C95500, Astm B584, C95800, C83600, C36000, C93200 Bronze, C93200, Leaded Bronze, Bronze Rod, Phosphor Bronze, C95400 Aluminum Bronze, Phosphorous Bronze, Uns C63000
Please contact us for all your needs of

Nickel Aluminum Bronze C63000

at best prices from India. We are the biggest foundry casting alloy indian manufacturers exporters foundries in Jamnagar of

Nickel Aluminum Bronze C63000


Aluminum Bronze Alloy C62400 Aluminum Bronze Alloy C62400 Silicon-Aluminum Bronze C64200 Silicon-Aluminum Bronze C64200
 Designed & maintained by:  www.conextechno.com 
Home | About Us | Products | Resources | Email | Contact Us | Sitemap
                   +