Brass Copper Fittings (INDIA) Home Email Sitemap
Home About Us Products Resources Email Contact Us Sitemap
Copper Turned Parts | Copper Fittings | Copper Pressed Parts | Copper Casting | Bronze Fittings | Copper Washers | Copper Bronze Grounding Parts | Bronze Casting | Copper Electrical Components | Brass Electrical Components | Brass Turned Parts | Brass Fasteners | Brass Casting | Copper Casting Alloys | Brass Wires Rods Alloys | Brass Hardware Fittings | Brass Sanitary Pipe Fittings | Brass Hose Fittings | Stainless Steel Fittings | Brass Moulding Inserts | Copper Lugs Terminals
Copper Turned Parts
Copper Fittings
Copper Pressed Parts
Copper Casting
Bronze Fittings
Copper Washers
Copper Bronze Grounding Parts
Bronze Casting
Copper Electrical Components
Brass Electrical Components
Brass Turned Parts
Brass Fasteners
Brass Casting
Copper Casting Alloys
Brass Wires Rods Alloys
Brass Hardware Fittings
Brass Sanitary Pipe fittings
Brass Hose Fittings
Stainless Steel Fittings
Brass Moulding Inserts
Copper Lugs Terminals
              Silicon-Aluminum Bronze C64200

Silicon-Aluminum Bronze C64200   Copper Alloy No. C64200   Silicon-Aluminum Bronze C64200

Silicon Aluminum Bronze, ASTM B150 CDA 642

Chemical Composition % by weight
Element Nominal Minimum Maximum
Copper 91.2 Rem. Rem.
Lead - - .05
Iron - - .30
Tin - - .20
Zinc - - .50
Aluminum 7 6.3 7.6
Manganese - - .10
Silicon 1.8 1.5 2.2
Nickel (incl. Co) - - .25
Arsenic - - .15
Applications
Valve stems, gears, marine hardware, pole line hardware, bolts, nuts, valve bodies and components.
Common Fabrication Processes
Hot forming, forging, machining.
Mechanical Properties
Typical for 1-1/2" Rod Hard (10%) Temper
Hardness* Rockwell F Scales 90
Tensile Strength** KSI 93
Yield Strength ** KSI 60
Elongation** % in 2 inch 26
**Test values are nominal approximations and depend on specimen size and orientation.
Physical Properties
Thermal Conductivity BTU/ (sq ft-ft-hr-F) 26
Specific Heat BTU/lb/ºF @ 68F .09
Thermal Expansion Per °F from 68 F to 212 F .0000100
Density lb/cu in @ 68 F .278
Electrical Conductivity % IACS @ 68 F 8
Modulus of Elasticity KSI 16,000
*Volume basis
Fabrication Practices
Capacity for being cold worked Poor
Capacity for being hot formed Excellent
Hot forgeability rating (forging brass =100) 80
Suitability for being joined by: Soldering/Not Recommended
Brazing/Fair
Oxyacetylene Welding/Not Recommended
Gas Shielded Arc Welding/Fair
Coated Metal Arc Welding/Fair
Resistance Welding Spot/Fair
Seam/Fair
Butt/Fair
The values listed above represent reasonable approximations suitable for general engineering use. Due to commercial variations in composition and to manufacturing limitations, they should not be used for specification purposes. See applicable A.S.T.M. specification references.

Bronze Alloys, Bronze Properties, Aluminum Alloys, Silicon Bronze Ingots, Aluminum, Copper Aluminum Alloys, Properties Of Bronze, Bronze Wire, Aluminium Bronze, Nickel Aluminum Bronze, Silicon Bronze, Phosphor Bronze Wire, Bronze Rod, Aluminium Copper Alloys, Beryllium Copper Alloys, Tantalum Wire, Nickel Silver Alloy, Nickel Alloys, Metal Alloys, Brass Alloys Related words : Bronze Alloys, Bronze Properties, Aluminum Alloys, Silicon Bronze Ingots, Aluminum, Copper Aluminum Alloys, Properties Of Bronze, Bronze Wire, Aluminium Bronze, Nickel Aluminum Bronze, Silicon Bronze, Phosphor Bronze Wire, Bronze Rod, Aluminium Copper Alloys, Beryllium Copper Alloys, Tantalum Wire, Nickel Silver Alloy, Nickel Alloys, Metal Alloys, Brass Alloys
Please contact us for all your needs of

Silicon-Aluminum Bronze C64200

at best prices from India. We are the biggest foundry casting alloy indian manufacturers exporters foundries in Jamnagar of

Silicon-Aluminum Bronze C64200


Nickel Aluminum Bronze C63000 Nickel Aluminum Bronze C63000 Manganese Bronze C67300 Manganese Bronze C67300
 Designed & maintained by:  www.conextechno.com 
Home | About Us | Products | Resources | Email | Contact Us | Sitemap
                   +