Brass Copper Fittings (INDIA) Home Email Sitemap
Home About Us Products Resources Email Contact Us Sitemap
Copper Turned Parts | Copper Fittings | Copper Pressed Parts | Copper Casting | Bronze Fittings | Copper Washers | Copper Bronze Grounding Parts | Bronze Casting | Copper Electrical Components | Brass Electrical Components | Brass Turned Parts | Brass Fasteners | Brass Casting | Copper Casting Alloys | Brass Wires Rods Alloys | Brass Hardware Fittings | Brass Sanitary Pipe Fittings | Brass Hose Fittings | Stainless Steel Fittings | Brass Moulding Inserts | Copper Lugs Terminals
Copper Turned Parts
Copper Fittings
Copper Pressed Parts
Copper Casting
Bronze Fittings
Copper Washers
Copper Bronze Grounding Parts
Bronze Casting
Copper Electrical Components
Brass Electrical Components
Brass Turned Parts
Brass Fasteners
Brass Casting
Copper Casting Alloys
Brass Wires Rods Alloys
Brass Hardware Fittings
Brass Sanitary Pipe fittings
Brass Hose Fittings
Stainless Steel Fittings
Brass Moulding Inserts
Copper Lugs Terminals
              Phosphor Bronze Alloy C54400

Phosphor Bronze Alloy C54400   Copper Alloy No. C54400   Phosphor Bronze Alloy C54400

Phosphor Bronze B-2 , ASTM B 139 CDA 544

Chemical Composition % by weight
Element Nominal Minimum Maximum
Copper 88 Rem. Rem.
Lead 4 3.5 4.5
Iron - - .10
Tin 4 3.5 4.5
Zinc 4 1.5 4.5
Phosphorus - .01 .50
Applications
Bearings, bushings, gears, pinions, shafts, thrust washers, valve parts.
Common Fabrication Processes
Blanking, drawing, forming and bending, machining, shearing, stamping.
Mechanical Properties
Typical for 1" dia. Rod Hard (25%) Temper
Hardness* Rockwell F Scales 80
Tensile Strength** KSI 68
Yield Strength ** KSI 57
Elongation** % in 2 inch 20
**Test values are nominal approximations and depend on specimen size and orientation.
Physical Properties
Thermal Conductivity BTU/ (sq ft-ft-hr-F) 50
Specific Heat BTU/lb/ºF @ 68F .09
Thermal Expansion Per °F from 68 F to 212 F .0000096
Density lb/cu in @ 68 F .321
Electrical Conductivity % IACS @ 68 F 19
Modulus of Elasticity KSI 15,000
*Volume basis
Fabrication Practices
Capacity for being cold worked Good
Capacity for being hot formed -
Suitability for being joined by: Soldering/Excellent
Brazing/Good
Oxyacetylene Welding/Not Recommended
Gas Shielded Arc Welding/Not Recommended
Coated Metal Arc Welding/Not Recommended
Resistance Welding Spot/Not Recommended
Seam/Not Recommended
Butt/Fair
The values listed above represent reasonable approximations suitable for general engineering use. Due to commercial variations in composition and to manufacturing limitations, they should not be used for specification purposes. See applicable A.S.T.M. specification references.

Phosphor Bronze, 932 Bronze, Nickel Silver Alloy, C360 Brass, C10100 Copper, Copper C11000, C14500, C95500, Astm B584, C83600, C36000, C95800, C93200 Bronze, C93200, Leaded Bronze, Bronze Rod, Phosphorous Bronze, Naval Brass, Aluminium Bronze, Bronze Alloys Related words : Phosphor Bronze, 932 Bronze, Nickel Silver Alloy, C360 Brass, C10100 Copper, Copper C11000, C14500, C95500, Astm B584, C83600, C36000, C95800, C93200 Bronze, C93200, Leaded Bronze, Bronze Rod, Phosphorous Bronze, Naval Brass, Aluminium Bronze, Bronze Alloys
Please contact us for all your needs of

Phosphor Bronze Alloy C54400

at best prices from India. We are the biggest foundry casting alloy indian manufacturers exporters foundries in Jamnagar of

Phosphor Bronze Alloy C54400


Phosphor Bronze Alloy C51000 Phosphor Bronze Alloy C51000 Aluminum Bronze Alloy C61400 Aluminum Bronze Alloy C61400
 Designed & maintained by:  www.conextechno.com 
Home | About Us | Products | Resources | Email | Contact Us | Sitemap
                   +